LMS-S008-CR-CP-780Y/980T Complex Phase — Cold Rolled Steel

LMS-S008-CR-CP-780Y/980T is a complex phase grade cold rolled steel conforming to the lucid material specifications. At 780 MPa minimum yield strength, this is hot-stamped-equivalent steel for critical occupant protection zones and maximum intrusion resistance, with very high tensile properties for peak structural performance in anti-intrusion and rollover protection members.

As a Complex Phase steel, LMS-S008-CR-CP-780Y/980T offers a specific combination of strength and formability engineered for advanced automotive manufacturing. The complex phase microstructure combines high strength with edge ductility for roll-formed and stretch-flanged parts.

Ameristeel maintains inventory of LMS-S008-CR-CP-780Y/980T in various gauges and widths, available as coils, sheets, or custom blanks. Our ISO 9001:2015 certified processes ensure consistent quality from prototype through production volumes.

Available coating options for LMS-S008-CR-CP-780Y/980T include Uncoated, Galvanized, Electrogalvanized, Galvannealed, Zinc Magnesium, providing corrosion protection and surface preparation suited to your manufacturing process requirements.

LMS-S008-CR-CP-780Y/980T at 780 MPa yield and 980 MPa tensile compares to LMS-S008-CR-DP-700Y/980T (80 MPa higher yield at 700 MPa and 980 MPa vs 980 MPa tensile) and LMS-S008-CR-MS-860Y/1100T (80 MPa lower yield at 860 MPa and 980 MPa vs 1100 MPa tensile). Selecting the right grade depends on the balance between strength requirements and forming complexity for your specific stamping application.