LMS-S008-CR-MS-1030Y/1300T Martensitic — Cold Rolled Steel

LMS-S008-CR-MS-1030Y/1300T is a martensitic grade cold rolled steel conforming to the lucid material specifications. At 1030 MPa minimum yield strength, this is extreme-performance martensitic steel for the most demanding anti-intrusion applications requiring peak load-bearing capacity, with extreme tensile strength for maximum occupant protection performance in the most severe crash scenarios.

As a Martensitic steel, LMS-S008-CR-MS-1030Y/1300T offers a specific combination of strength and formability engineered for advanced automotive manufacturing. The predominantly martensitic microstructure delivers the highest strength levels for anti-intrusion and structural reinforcement.

Ameristeel maintains inventory of LMS-S008-CR-MS-1030Y/1300T in various gauges and widths, available as coils, sheets, or custom blanks. Our ISO 9001:2015 certified processes ensure consistent quality from prototype through production volumes.

Available coating options for LMS-S008-CR-MS-1030Y/1300T include Uncoated, Galvanized, Electrogalvanized, Galvannealed, Zinc Magnesium, providing corrosion protection and surface preparation suited to your manufacturing process requirements.

LMS-S008-CR-MS-1030Y/1300T at 1030 MPa yield and 1300 MPa tensile compares to LMS-S008-CR-MS-860Y/1100T (170 MPa higher yield at 860 MPa and 1300 MPa vs 1100 MPa tensile) and LMS-S008-CR-MS-1220Y/1500T (190 MPa lower yield at 1220 MPa and 1300 MPa vs 1500 MPa tensile). Selecting the right grade depends on the balance between strength requirements and forming complexity for your specific stamping application.